API API-571 - Corrosion and Materials Professional

API RP 571 – Sulfidation:

“Sulfidation generally results in uniform thinning of iron-based alloys at temperatures above 500°F (260°C).”

“It is classified as a form of general corrosion, although it can be accelerated in turbulent flow areas.”

So, option A is correct.

API RP 571 states under the section Phosphoric Acid Corrosion:

“Corrosion usually occurs when the acid dries out and forms concentrated phosphoric acid deposits, which are very aggressive to carbon steel.”

“Drying or concentration occurs due to poor flow distribution or operational upsets. Localized areas may experience acid concentration due to vaporization.”

(Reference: API RP 571, Section 4.3.3.8 – Phosphoric Acid Corrosion)

Therefore, the most aggressive corrosion occurs when the acid dries out, making option D correct.

API RP 571, in its discussion on Wet Hâ‚‚S Damage, including HIC, SOHIC, and SSC, consistently identifies a shared mechanism:

“All wet H₂S-related damage mechanisms involve the absorption of atomic hydrogen, formed at the steel surface by the corrosion reaction in the presence of H₂S.”

“The absorbed hydrogen may diffuse into the steel, accumulate at trap sites, and cause cracking or blistering.”

(Reference: API RP 571, Section 4.2.2.7 – Wet H₂S Damage Mechanisms)

Thus, hydrogen absorption and permeation is a unifying mechanism across all these damage modes. Therefore, option D is correct.

As per API RP 945 (4th Edition, 2022):

“Post-weld heat treatment (PWHT) is the most effective method for reducing residual stresses that contribute to amine SCC. PWHT minimizes the stress intensity required for crack initiation and growth.”

Lowering temperature helps but is not always feasible.

Water content and amine concentration affect SCC but are not as impactful as PWHT.

Thus, Option A (Post-weld heat treatment) is the most effective mitigation.